Optical glass, glass preform and optical element

ABSTRACT

The invention provides a high-refraction low-dispersion optical glass with low material cost, refractive index of 1.77-1.85, and Abbe number of 40-48, wherein the following components by weight percentage: 4-20% of SiO 2 , 8-24% of B 2 O 3 , 20-40% of La 2 O 3 , 11-30% of Gd 2 O 3 , 0-15% of Y 2 O 3 , 0-8% of TiO 2 , 0-8% of Ta 2 O 5 , more than 0 but less than or equal to 8% of Nb 2 O 5 , less than 1 of Ta 2 O 5 /Nb 2 O 5 , more than 0 but less than or equal to 15% of ZrO 2 , and 11-30% of ZnO. The invention reduces the content of Ta 2 O 5  and optimizes the cost of raw materials; through rational composition design, the optical glass of the invention is conducive to precision molding while achieving the required optical constant, with excellent chemical stability. A glass preform and an optical element made of the optical glass are also disclosed.

TECHNICAL FIELD

The present invention relates to a high-refractivity and low-dispersion optical glass, in particular to a high-refractivity and low-dispersion optical glass and optical element.

BACKGROUND

In recent years, with the rapid development of digitization and high precision of the optical system, in the optical equipment such as digital camera, video camera and other photographic equipment as well as image playback (projection) equipment such as projector and projection television, higher and higher requirements are imposed on overall lightweight and miniaturization of optical system for reducing the number of optical elements like lens and prism therein. In the design of the optical system, the extensive use of high-refractivity glass or the use of non-spherical lens is applied to achieve miniaturization, ultra-thin and wide-angle, to realize lightweight and high-performance of optical system while easier to achieve color correction, thus high-refractivity low-dispersion glass research and development needs are gradually increased.

Early production of high-refractivity low-dispersion glass contains a large amount of Ta₂O₅. For example, CN1876589A discloses an optical glass with refractive index of 1.75-1.85 and Abbe number of 34-44, which contains more than 15% but less than 35% of Ta₂O₅. Tantalum is a scarce metal, and the use of Ta₂O₅ is extremely unfavorable for the product cost control, so the research and development objective of optical glass workers is to reduce or not use Ta₂O₅ in the high-refractivity low-dispersion glass composition.

SUMMARY

A technical problem to be solved by the present invention is to provide a high-refractivity low-dispersion optical glass with low material cost, refractive index of 1.77-1.85 and Abbe number of 40-48.

The present invention also provides a glass preform and an optical element made of the above optical glass.

To solve the technical problem, the technical scheme of the present invention provides: (1) An optical glass, comprising the following components by weight percentage:

4-20% of SiO₂;

8-24% of B₂O₃;

20-40% of La₂O₃;

11-30% of Gd₂O₃;

0-15% of Y₂O₃;

0-8% of TiO₂;

0-8% of Ta₂O₅;

more than 0 but less than or equal to 8% of Nb₂O₅;

less than 1 of Ta₂O₅/Nb₂O₅;

more than 0 but less than or equal to 15% of ZrO₂;

11-30% of ZnO.

(2) The optical glass according to (1), comprising the following components by weight percentage:

0-15% of WO₃;

0-10% of Al₂O₃;

0-10% of Yb₂O₃;

0-2% of Li₂O;

0-10% of Na₂O;

0-10% of K₂O;

0-1% of Sb₂O₃;

0-10% of RU, in which RO is one or more of MgO, CaO, SrO or BaO.

(3) An optical glass, comprising the following components by weight percentage:

4-20% of SiO₂;

8-24% of B₂O₃;

20-40% of La₂O₃;

11-30% of Gd₂O₃;

0-15% of Y₂O₃;

0-15% of WO₃;

0-8% of Ta₂O₅;

more than 0 but less than or equal to 8% of Nb₂O₅;

less than 1 of Ta₂O₅Nb₂O₅;

more than 0 but less than or equal to 15% of ZrO₂;

11-30% of ZnO;

0-8% of TiO₂;

0-10% of Al₂O₃;

0-10% of Yb₂O₃;

0-2% of Li₂O;

0-10% of Na₂O;

0-10% of K₂O;

0-1% of Sb₂O₃;

0-10% of RO, in which RO is one or more of MgO, CaO, SrO or BaO.

(4) The optical glass according to any of claims (1)-(3), wherein the content of each component satisfies one or more of the following 9 conditions;

{circle around (1)} Ta₂O₅/Nb₂O₅ is less than 0.8;

{circle around (2)} ZnO/(SiO₂+B₂O₃) is 0.3-2;

{circle around (3)} Gd₂O₃/(La₂O₃+Gd₂O₃+Y₇O₃) is 0.2-0.

{circle around (4)} SiO₂/(SiO₂+B₂O₃) is 0.2-0.6;

{circle around (5)} Nb₂O₅/Gd₂O₃ is 0.01-0.45;

{circle around (6)} (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂) is 0.1-5;

{circle around (7)} Nb₂O₅/ZnO is 0.01-0.5;

{circle around (8)} TiO₂/(TiO₂+Nb₂O₅) is 0.01-0.8;

{circle around (9)} ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂) is above 1.8.

(5) The optical glass according to any of claims (1)-(3), further comprising: 5-18% of SiO₂, and/or 10-23% of B₂O₃, and/or 20-35% of La₂O₃, and/or 11-25% of Gd₂O₃, and/or 0-10% of Y₂O₃, and/or 0-10% of WO₃, and/or 0-5% of Ta₂O₅, and/or 0.1-6% of Nb₂O₅, and/or 1-10% of ZrO₂, and/or 15-30% of ZnO; and/or 0-5% of TiO₂; and/or 0-5% of Al₂O₃; and/or 0-5% of Yb₇O₃; and/or 0-1% of Li₂O, and/or 0-5% of Na₂O; and/or 0-5% of K₇O; and/or 0-0.5% of Sb₂O₃, and/or 0-5% of RO, in which RO is one or more of MgO, CaO, SrO or BaO.

(6) The optical glass according to any of claims (1) to (3), further comprising: 6-15% of SiO₂, and/or 12-20% of B₂O₃, and/or 22-32% of La₂O₃, and/or 12-22% of Gd₂O₃, and/or 0-8% of Y₂O₃, and/or 0-7% of WO₃, and/or 2-8% of ZrO₂, and/or 15-25% of ZnO, and/or 0-2% of TiO₂.

(7) The optical glass according to any of claims (1) to (3), further comprising: less than 0.5 of Ta₂O₅/Nb₂O₅, and/or 0.5-1.8 of ZnO/(SiO₂+B₂O₃), and/or 0.25-0.5 of Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃, and/or 0.23-0.5 of SiO₂/(SiO₂+B₂O₃), and/or 0.02-0.35 of Nb₂O₅/Gd₂O₃, and/or 0.1-3 of (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂), and/or 0.02-0.35 of Nb₂O₅/ZnO, and/or 0.05-0.7 of TiO₂/(TiO₂+Nb₂O₅), and/or 3-15 of ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂).

(8) The optical glass according to any of claims (1) to (3), further comprising: 0.5-1.45 of ZnO/(SiO₂+B₂O₃); and/or 0.25-0.45 of Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃), and/or 0.25-0.45 of SiO₂/(SiO₂+B₂O₃), and/or 0.05-0.25 of Nb₂O₅/Gd₂O₃, and/or 0.1-1 of (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂), and/or 0.03-0.25 of Nb₂O₅/ZnO, and/or 0.1-0.6 of TiO₂/(TiO₂+Nb₂O₅), and/or 4-12 of ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂).

(9) The optical glass according to any of claims (1) to (3), wherein: the total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O₅, WO₃, ZrO₂ and ZnO is above 95%, excluding Ta₂O₅.

(10) The optical glass according to any of claim (9), wherein: the total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O, ZrO₂ and ZnO is above 99%.

(11) The optical glass according to (1) or (2), comprising the following components by weight percentage:

0-10% of P₂O₅;

0-10% of Bi₂O₃;

0-10% of TeO₂;

0-10% of Ga₂O₃;

0-10% of Lu₂O₃;

0-8% of GeO₂;

0-1% of CeO₂;

0-1% of SnO₂;

0-10% of F.

(12) The optical glass according to (1) or (2), comprising the following components by weight percentage:

0-5% of P₂O₅;

0-5% of Bi₂O₃;

0-5% of TeO₂;

0-5% of Ga₂O₃;

0-5% of Lu₂O₃;

0-5% of GeO₂;

0-0.5% of CeO₂;

0-0.5% of SnO₂;

0-5% of F.

(13) The optical glass according to any of (1) to (12), wherein the refractive index (nd) of the glass is 1.77-1.85, the Abbe number (vd) is 40-48, and the density (p) of the glass is below 5.00 g/cm³.

(14) The optical glass according to any of (1) to (12), wherein the corresponding wave length λ₈₀ is below 410 nm when the transmittance of the glass reaches 80%, the corresponding wave length λ₅ is below 350 nm when the transmittance reaches 5%, the upper limit of devitrification temperature is below 1160° C., and the glass transition temperature (Tg) is below 630° C.

(15) The optical glass according to any of (1) to (12), wherein the corresponding wave length λ₈₀ is below 400 nm when the transmittance of the glass reaches 80%, the corresponding wave length λ₅ is below 340 nm when the transmittance reaches 5%, the upper limit of devitrification temperature is below 1150° C., the glass transition temperature (Tg) is below 620′C, and the density (ρ) of the glass is below 4.90 g/cm³.

(16) A glass preform, made of the optical glass according to (1) to (15).

(17) An optical element, made of the optical glass according to (1) to (15).

The advantages of the present invention are as follows: reduce the content of Ta₂O₅ and optimize the cost of raw materials; through rational composition design, the optical glass of the invention is conducive to precision molding while achieving the required optical constant, with excellent chemical stability. A glass preform and an optical element made of the optical glass are also disclosed.

DETAILED DESCRIPTION

I. Optical Glass

The optical glass of the present invention reduces or does not contain expensive Ta₂O₅ content in consideration of reducing the cost of raw materials, to obtain a high-refractivity low-dispersion optical glass having a refractive index of 1.77-1.85 and an Abbe number of 40-48.

The composition of the optical glass according to the present invention will be described in detail below, and the content and the total content of each glass component are expressed by weight percentage unless otherwise specified. In the following description, if referred to below or above the prescribed value, the prescribed value is included.

B₂O₃ is a glass network forming component having an effect of improving glass fusibility and devitrification resistance and reducing glass transition temperature and density. In order to achieve the above-mentioned effects, the present invention introduces 8% or more of B₂O₃, preferably introducing more than 10% of B₂O₃, more preferably introducing more than 12% of B₂O₃. However, when the introduced amount is more than 24%, the glass stability will be lowered and the refractive index will be lowered, so that the high refractive index of the present invention cannot be obtained. Therefore, the content of B₂O₃ is set to an upper limit of 24% in the present invention, preferably an upper limit of 23%, and more preferably an upper limit of 20%.

SiO₂ is also a glass forming body, which is different from the loose chain layered network formed by B₂O₃. SiO₂ forms silica-oxygen tetrahedron three-dimensional network in the glass, being very dense and solid. This network is added into the glass to reinforce the loose boron oxide triangular body [BO₃] network to make it dense, thereby enhancing the high temperature viscosity of the glass; at the same time, the addition of the silicon tetrahedron three-dimensional network and the improved capability of glass network isolation from devitrification cations such as La, Nb and Li increase the devitrification threshold, so that the lower limit of SiO₂ content in the glass of the present invention is 4%, preferably 5%, more preferably 6% when the above effect is better; but if the content of SiO₂ is too large, the glass transition temperature will be increased and the meltability of the glass will be lowered, so that the upper limit of the content is 20%, preferably the upper limit of 18%, further preferably the upper limit of 15%.

The present invention not only can increase the meltability of the glass by controlling the ratio of SiO₂ content to the content of SiO₂ and ₂O₃ (SiO₂/(iO₂+B₂O₃)) within 0.2-0.6, but also can effectively increase the glass stability and high temperature viscosity. Especially when the SiO₂/(iO₂+B₂O₃) value is 0.23-0.5, the devitrification resistance performance can be effectively improved while maintaining the high-refraction low-dispersion optical properties and low transition temperature characteristics of the glass, further preferably 0.25-0.45.

La₂O₃ is an essential component for obtaining the optical properties required for the present invention. In the formulation system of the present invention, the combination of B₂O₃ and La₂O₃ can effectively improve the devitrification resistance of the glass and improve the chemical stability of the glass. When the La₂O₃ content is less than 20%, it is difficult to achieve the required optical properties; but when its content exceeds 40%, the glass resistance to devitrification and melting properties are deteriorated. Thus, the La₂O₃ content of the present invention is 20-40%, preferably in the range of 20-35%, more preferably in the range of 22-32%.

Gd₂O₃ can increase the refractive index of the glass, but not significantly improving the dispersion of the glass. By introducing over 11% of Gd₂O₃ to coexist with La₂O₃ in the present invention, the stability of the glass can be improved, the chemical stability of the glass can be remarkably enhanced, and the excessive rise of the Abbe number can be controlled while maintaining the refractive index. If the content exceeds 30%, the glass devitrification resistance will be reduced and the density of the glass will be increased. Therefore, the Gd₂O₃ content of the present invention is 11-30%, preferably in the range of 11-25%, more preferably in the range of 12-22%.

The high-refraction and low-dispersion component of the present invention is also preferably introduced into Y₂O₃, which suppresses the rise in the cost of the glass material while maintaining the high refractive index and high Abbe number, and improves the meltability and devitrification resistance of the glass. In addition, it can reduce the upper limit of devitrification temperature of the glass and specific gravity, but if its content exceeds 15%, the glass stability and devitrification resistance will be decreased. Thus, the Y₂O₃ content is in the range of 0-15%, preferably in the range of 0-10%, more preferably 0-8%.

Yb₂O₃ is also a component which imparts high refraction and low dispersion properties. When the introduced amount thereof is more than 10%, the anti-devitrification property of the glass will be lowered, so that the content thereof is limited to 0-10%, preferably 0-5%.

In the present invention, La₂O₃ coexists with Gd₂O₃, or preferably La₂O₃ and Gd₂O₃ coexist with Y₂O₃, more preferably Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is in the range of 0.2-0.55, further preferably Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) in the range of 0.25-0.5, furthermore preferably Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) in the range of 0.25-0.45. It is possible to overcome the undesirable effect of reducing the stability of the glass due to the reduction or non-use of Ta₂O₅ to obtain the high-refraction low-dispersion glass with excellent glass stability, while the glass is not easy to be colored.

In the glass of the present invention, when the content of Nb₂O₅ exceeds 0, it has an excellent effect in lowering the liquidus temperature, and also has the effect of improving the glass refractive index, the anti-devitrification property and the chemical durability without deteriorating the transmittance. By introducing appropriate amount of Nb₂O₅, it can effectively improve the glass anti-devitrification properties in the precision molding process. If its content exceeds 8%, the glass dispersion will be increased, so as not to achieve the optical properties of the glass in the present invention. Thus, the Nb₂O₅ content is in the range of more than 0 but less than or equal to 8%, preferably in the range of 0.1-6%. The inventors of the present invention have found that when the ratio of Nb₂O₅ content to Gd₂O₃ content (Nb₂O₅/Gd₂O₃) in the glass of the present invention is 0.01-0.45, it can significantly improve the chemical durability and devitrification resistance of the glass, and in particular, when the Nb₂O₅/Gd₂O₃ value is 0.02-0.35, the effect is particularly conspicuous, further preferably 0.05-0.25.

Ta₂O₅ can improve the refractive index and devitrification resistance of the glass as well as viscosity of the molten glass, but it is expensive and is disadvantageous to the reduction of raw material costs. Therefore, its content is limited to be less than 8%, preferably less than 5%, more preferably less than 1%, further preferably not added.

In the present invention, the value of Ta₂O₅/Nb₂O₅ is controlled to be less than 1, which can improve the anti-devitrification property of the glass while effectively adjusting the refractive index and dispersion. In addition, when the glass contains an easily colored component, the value of Ta₂O₅/Nb₂O₅ is preferably less than 0.8, which can effectively improve the coloring property of glass, the value of Ta₂O₅/Nb₂O₅ is further preferably less than 0.5, and the value of Ta₂O₅/Nb₂O₅ is furthermore preferably less than 0.3.

ZnO is added to the glass of the present invention system, the refractive index and dispersion of the glass can be adjusted, the anti-devitrification performance of the glass can be improved, the glass transition temperature can be reduced and the stability of the glass can be enhanced. Besides, ZnO can also reduce the high temperature viscosity of the glass, so that the glass can be smelt at lower temperatures, which can enhance the glass transmittance. In particular, when a small amount of tantalum oxide or even no tantalum oxide is contained in the glass of the present invention, it is possible to compensate for the reduction of the optical constant to a certain extent by introducing over 11% of ZnO. However, if the amount of ZnO is added too much, the glass's anti-devitrification properties will decline, while the high temperature viscosity is small, bringing challenge to molding. In the glass system of the present invention, if the content of ZnO is less than 11%, the Tg temperature cannot meet the design requirements. If the content is higher than 30%, the anti-devitrification property of the glass will decrease and the high temperature viscosity cannot meet the design requirements. Therefore, the lower limit of the ZnO content is limited to 11%, preferably with lower limit to 15%; the upper limit of the ZnO content is limited to 30%, preferably with upper limit to 25%.

In order to obtain an easy-melting glass having a relatively low Tg temperature and good stability, the inventors of the present invention have found through a large number of experimental studies that, when the ratio of ZnO/(B₂O₃+SiO₂) is in the range of 0.3-2, preferably the ratio of ZnO/(B₂O₃+SiO₂) in the range of 0.5-1.8, further preferably the ratio of ZnO/(B₂O₃+SiO₂) in the range of 0.5-1.45, the glass stability and Tg temperature can reach the best balance to get better quality products.

Meanwhile, in order to give the glass an excellent anti-devitrification property at a suitable Tg temperature, it is preferred to control the value of Nb₂O₅/ZnO in the range of 0.01-0.5, further preferably 0.02-0.35, furthermore preferably 0.03-0.25.

ZrO₂ is a high-refraction low-dispersion oxide, which can enhance the refractive index of glass and adjust the dispersion if added into the glass. At the same time, the appropriate amount of ZrO₂ is added into the glass, which can enhance the glass's anti-devitrification property and glass forming stability. In the present invention, if the content is higher than 15%, the glass becomes difficult to melt, and the melting temperature increases, the inclusions and the transmittance of the glass are likely to decrease. Therefore, the ZrO₂ content is more than 0 but less than or equal to 15%, preferably 1-10%, and further preferably 2-8%.

TiO₂ is a high-refraction high-dispersion oxide, which can significantly enhance the glass refractive index and dispersion if added into the glass. The inventors of the present invention have found that it is possible to increase the glass stability, particularly the anti-devitrification property, by adding the appropriate amount of TiO₂ into the glass of the present invention. However, if the TiO₂ is added too much, it will be difficult to achieve the development target of low dispersion, and also, the transmittance of glass will be significantly reduced and the stability of the glass will deteriorate. Therefore, the content of TiO₂ is 0-8%, preferably 0-5%, and more preferably 0-2%. In the present invention, the ratio of TiO₂/(TiO₂+Nb₂O₅) is controlled to 0.01-0.8, by which the devitrification performance and chemical durability of the glass can be effectively adjusted, more preferably TiO₂/(TiO₂+Nb₂O₅) to 0.05-0.7, and further preferably TiO₂/(TiO₂+Nb₂O₅) to 0.1-0.6.

WO₃ is mainly used to maintain the optical constant in glass and improve glass devitrification, but if the content of WO₃ is too high, the transmissivity of glass will reduce, staining degree will increase and devitrification property is liable to be poor. Thus, the content of WO₃ is 0-15%, more preferably 0-10%, and further preferably 0-7%.

The excessive introduction of WO₃ and TiO₂ will reduce the transmittance of the glass, but both of them have a good effect on the anti-devitrification properties of glass. It is found through the inventors' research on the optical glass of the system that, when (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂) is controlled within 0.1-5, this not only can well meet the balance of transmittance and devitrification performance, but also can further optimize the chemical stability of the glass. The value of (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂) is further preferably 0.1-3, and the value of (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂) furthermore preferably 0.1-1.

In particular, in order to ensure that the glass has a good transmittance and a low cost advantage while maintaining the optical properties of the glass with excellent anti-devitrification property and high refraction as well as low dispersion, it is found from a large number of experimental studies that the aforementioned goal can be achieved by controlling ZnO/(WO₃+Ta₂O+Nb₂O₅+TiO₂) above 1.8, preferably 3-15, furthermore preferably 4-12.

By introducing small amount of Al₂O₃, it can improve the stability and chemical stability of the glass. However, when the content exceeds 10%, the glass has a tendency to deteriorate the melt property and reduce the devitrification resistance. Therefore, the content of Al₂O₃ in the present invention is 0-10%, preferably 0-5%, more preferably 0-1%, and further preferably not introduced.

The addition of Li₂O into the glass component can effectively reduce the Tg temperature of the glass, but the optical glass with low softening point is usually smelted with platinum or platinum alloy vessels. During high temperature smelting, Li⁺ in the glass component easily corrodes platinum or platinum alloy vessels, resulting in more platinum-containing foreign matters in the finished glass, leading to a decline in the quality of the glass. In addition, more than 2% of Li₂O in the present invention causes a sharp decrease in the devitrification performance of the glass, and therefore, the content thereof is limited to 0-2%, preferably 0-1%.

Na₂O and K₂O are any components effective for reducing the Tg, and if the content thereof is too large, it is easy to cause the devitrification temperature to be increased and hard to be vitrified, so that the contents thereof are limited to 0-10%, more preferably 0-5%, and further preferably 0-1% respectively.

RO (RO is one or more of MgO, CaO, SrO or BaO) can improve the meltability of the glass and adjust the optical property of the glass, but when its content exceeds 10%, the devitrification resistance of the glass will be lowered. The RO content of the present invention is 0-10%, more preferably 0-5%, and further preferably not introduced.

P₂O₅ is an optional component for improving the devitrification resistance of the glass, and particularly when the content of P₂O₅ is less than 10%, the chemical durability of the glass, particularly the decrease in water resistance, can be suppressed. Therefore, the content of the glass is preferably less than 10%, preferably less than 5%, more preferably less than 3%, and further preferably not introduced, with respect to the total mass of the glass composed by oxide conversion.

Bi₂O₃ is an optional component capable of properly increasing the refractive index of glass and lowering the vitrification temperature, and when its content exceeds 10%, the glass devitrification resistance will be lowered, so that its content is limited to be less than 10%, preferably less than 5%, further preferably less than 1%, and furthermore preferably not introduced.

GeO₂ is a component having an effect of increasing the refractive index of the glass and increasing the resistance to devitrification, and is an optional component of the optical glass of the present invention. However, it is expensive and excessive introduction cannot achieve the purpose of reducing the production cost. Thus, the content thereof is preferably less than 8%, preferably less than 5%, further limited to less than 2%, and furthermore preferably not introduced.

According to the present invention, if Lu₂O₃ is introduced in an amount of less than 10%, it can be used in combination with other rare earth components to further improve the stability of the glass, but it is expensive and is not conducive to reducing the production cost if introduced in the glass. Therefore, the content thereof is limited to be less than 10%, preferably less than 5%, further preferably less than 3%, and furthermore preferably not introduced.

As an optional component of the present invention, when Ga₂O₃ is controlled to be less than 10%, the devitrification resistance of the glass can be improved, and the wear degree of the glass can be increased. Therefore, the content thereof is preferably less than 10%, further preferably less than 5%, furthermore preferably less than 3%, and further preferably not introduced.

TeO₂ is an optional component to improve the refractive index of glass and reduce the glass transition temperature of the glass. When its content thereof is too large, it is easy to have platinum crucible reaction, which is not conducive to the service life of the equipment. Therefore, the TeO₂ content is limited to be less than 10%, preferably less than 5%, and more preferably not introduced.

The addition of few Sb₂O₃, SnO₂ and CeO₂ components can improve the clarification effect of glass. However, when Sb₂O₃ content exceeds 1%, the glass has a tendency to clarify the performance degradation, and because of its strong oxidation, it promotes the corrosion of platinum or platinum alloy vessel for melting glass and the deterioration of the molding die. Therefore, the addition amount of Sb₂O₃ is preferably 0-1%, more preferably 0-0.5%, and further preferably not introduced. SnO₂ may also be added as a clarifying agent, but when the content thereof exceeds 1%, the glass may be colored, or when the glass is heated, softened, and molded, etc. Sn will become a starting point for nucleation, resulting in a tendency for devitrification. Therefore, the SnO₂ content of the present invention is preferably 0-1%, more preferably 0-0.5%, and further preferably not added. The role and the proportion of added amount of CeO₂ are consistent with SnO₂, so the content of CeO₂ is preferably 0-1%, more preferably 0-0.5%, and further preferably not added.

F is an effective component that is low in dispersion and reduces the glass transition temperature, but when it is excessively contained, the glass refractive index will be significantly reduced or the volatility of the glass melt will be increased, and texture will be produced during glass melt forming, or the tendency to increase the refractive index changes will be caused by volatilization. F, as a raw material, can be introduced by YF₃, LaF₃, GdF₃, ZrF₄, ZnF₂, alkali fluoride or alkaline earth fluoride. Preferably, the content of F in the present invention accounts for 0-10% of total content of optical glass, more preferably 0-5%, and further preferably not introduced.

In order to achieve the object of the present invention, the component of the glass is represented by weight percentage. The total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O₅, WO₃, ZrO₂ and ZnO is preferably above 95%, excluding Ta₂O₅; the total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O₅, WO₃, ZrO₂ and ZnO is more preferably above 99%, and the total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O₅, ZrO₂ and ZnO is further preferably above 99%.

[About the Ingredients that should not be Included]

The other components not mentioned above can be added as required without impairing the glass characteristics of the present invention. However, for the transition metal components such as V, Cr, Mn, Fe, Co, Ni, Cu, Ag, and Mo, even if they are contained in a single or compound form, the glass could be colored and absorb at a specific wavelength in the visible light region, thereby impairing the properties of the present invention in improving the visible light transmittance, and therefore, in particular, for optical glass with requirement on wavelength transmittance in the visible region, it is preferably not actually included.

Pb, Th, Cd, TI, Os, Be, and Se cations have been used in a controlled manner as a harmful chemical substance in recent years, which is necessary not only in the glass manufacturing process, but also in the manufacturing procedure and disposal after the productization for environmental protection measures. Therefore, in the case of attaching importance to the influence on the environment, it is preferably not actually included except for the inevitable incorporation. As a result, the optical glass does not actually contain a substance that contaminates the environment. Therefore, the optical glass of the present invention can be manufactured, processed, and discarded even if a measure is not taken as a special environmental countermeasure.

Hereinafter, the characteristics of the optical glass of the present invention will be described.

[Optical Constant of Optical Glass]

The optical glass of the present invention is a high-refraction low-dispersion glass, and a lens made of the high-refraction low-dispersion glass is combined with a lens made of high-refraction high-dispersion glass for chromatic aberration correction. The optical glass of the present invention has a glass refractive index (nd) in the range of 1.77-1.85, preferably in the range of 1.78-1.84, more preferably in the range of 1.785-1.84, from the viewpoint of imparting optical properties suitable for its use. The range of the Abbe number (ν_(d)) of the glass is in the range of 40-48, preferably in the range of 41-47.

[Transition Temperature of Optical Glass]

The optical glass will gradually turn from solid state to plastic state within a certain temperature range. The transition temperature refers to the temperature at which the glass sample is heated from room temperature to the sag temperature, and the temperature corresponding to the intersection of the low temperature region and the straight line extension of the high temperature region.

The glass of the present invention has a transition temperature (Tg) of below 630° C., preferably below 620° C., more preferably below 615° C., and further preferably below 610° C.

[Coloring of Optical Glass]

The short-wave transmission spectrum characteristics of the glass of the present invention are represented by pigmentation degree (λ₈₀/λ₅). Λ₈₀ refers to a wavelength corresponding to a glass transmittance of 80%, and λ₅ is a wavelength corresponding to a glass transmittance of 5%. The measurement of λ₈₀ is carried out using a glass having a thickness of 10±0.1 nm with two opposing planes parallel to each other and optically polished, measuring the spectral transmittance in the wavelength region from 280 nm to 700 nm nm and a wavelength exhibiting 80% of the transmittance. The spectral transmittance or transmittance is an amount indicated by I_(out)/I_(in) in the case where light of the intensity I_(in) is incident perpendicularly to the above surface of the glass, passes through the glass and emits light of the intensity I_(out) from one plane, including the transmittance of the surface reflection loss on the above surface of the glass. The higher the refractive index of the glass, the greater the surface reflection loss. Thus, in high refractive index glass, a small value of λ₈₀ means that the glass itself is colored very little.

The optical glass λ₈₀ of the present invention is less than or equal to 410 nm, preferably λ₈₀ is in the range of less than or equal to 405 nm, more preferably λ₈₀ is less than or equal to 400 nm, and further preferably λ₈₀ is less than or equal to 395 nm, and furthermore preferably λ₈₀ is less than or equal to 390 nm. λ₅ is less than or equal to 350 nm, preferably λ₅ is in the range of less than or equal to 345 nm, more preferably λ₅ is less than or equal to 340 nm, and further preferably λ₅ is less than or equal to 335 nm.

[The Density of Optical Glass]

The density of the optical glass is the mass per unit volume at a temperature of 20° C., expressed in g/cm³.

The density (ρ) of the glass of the present invention is below 5.00 g/cm³, preferably below 4.90 g/cm³.

[Upper Limit of Devitrification Temperature]

The devitrification performance of the glass is measured by the temperature gradient furnace method. The glass is made into a sample of 180*10*10 mm. The side surface is polished and placed in a furnace with a temperature gradient for 4 hours before taking out. The glass devitrification is observed under a microscope. The highest temperature corresponding to the glass crystal is the upper limit of devitrification temperature of the glass. The lower the upper limit of devitrification temperature of glass is, the stronger the stability of glass under high temperature will be and the better production process performance will achieve.

The devitrification temperature of the glass of the present invention is below 1160° C., preferably below 1155° C., further preferably below 1150° C., and furthermore preferably below 1140° C.

II. Glass Preform and Optical Element

Hereinafter, an optical preform and an optical element of the present invention will be described.

The glass preform and the optical element of the present invention are both formed by the optical glass of the present invention described above. The glass preform of the present invention has a high refractive index and low dispersion. The optical element of the present invention has a high refractive index and low dispersion, which can provide optical elements such as various lenses and prisms having a high optical value at a low cost.

Examples of the lens include various lenses such as concave meniscus lens, convex meniscus lens, biconvex lens, biconcave lens, planoconvex lens, and planoconcave lens.

This lens is combined with a lens made of high-refraction high-dispersion glass to correct the chromatic aberration, suitable as a lens for chromatic aberration correction. In addition, the lens is also effective for the compactness of the optical system.

In addition, for the prism, due to the high refractive index, by combining in the optical system, you can achieve a compact wide-angle optical system through the curved optical path, towards the desired direction.

Embodiments

The present invention is explained by the following embodiments, but the present invention should not be limited to these embodiments.

The method of melting and molding optical glass can be carried out by a technique known to those skilled in the art. Weigh the glass raw materials (carbonate, nitrate, sulfate, hydroxide, oxide, boric acid, etc.) in the proportions of the glass oxides and mix evenly, then put into a smelting device (such as a platinum crucible), cool to below 1250° C. after appropriate mixing, clarification and homogenization at 1150-1400° C., pour or leak in a molding die, and finally experience post-processing by annealing, processing, etc., or complete compression molding directly with precision profiling technology.

[Optical Glass Embodiment]

In addition, the characteristics of each glass of the present invention are measured by the following methods, and the measurement results are shown in Tables 1 to 6, wherein K1 represents Ta₂O₅/Nb₂O₅, K2 represents SiO₂/(SiO₂+B₂O₃), K3 represents Nb₂O₅/Gd₂O₃, K4 represents Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃), K5 represents (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂), K6 represents ZnO/(SiO₂+B₂O₃), K7 represents Nb₂O₅/ZnO, K8 represents TiO₂/(TiO₂+Nb₂O₅) and K9 represents ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂).

(1) Refractivity (nd) and Abbe number (vd)

The refractive index and Abbe number are measured as per the method specified in GB/T7962.1-2010.

(2) Pigmentation degree of glass (λ₈₀/λ₅)

The spectral transmittance is measured by using a glass sample having a thickness of 10±0.1 nm with two opposing planes parallel to each other and optically polished, and calculated on the basis of the result.

(3) Transition temperature of glass (Tg)

It is measured as per the method specified in GB/T7962.16-2010.

(4) The density of glass (p)

It is measured as per the method specified in GB/T7962.20-2010.

(5) Upper limit of devitrification temperature

The devitrification performance of the glass is measured by the temperature gradient furnace method. The glass is made into a sample of 180*10*10 mm. The side surface is polished and placed in a furnace with a temperature gradient for 4 hours before taking out. The glass devitrification is observed under a microscope. The highest temperature corresponding to the glass crystal is the upper limit of devitrification temperature of the glass.

(6) Devitrification in Glass Molding

After melting, clarification and homogenization, glass is molded into a block or molded material by flowing into the molding die through a platinum or platinum alloy discharge pipe. Then, observe the inside and the surface of the glass after cooling, and the appearance of crystal inside or on the surface of the glass indicates insufficient performance of glass devitrification. Express with “A” if no devitrification crystal appears inside or on the surface; express with “O” if devitrification crystal appears inside or on the surface.

TABLE 1 Embodiment Composition 1 2 3 4 5 SiO₂ 5.24 4.35 7.51 10.25 14.35 B₂O₃ 15.32 12.62 15.28 20.40 14.50 La₂O₃ 28.41 32.25 28.34 20.34 25.34 Gd₂O₃ 18.20 15.37 17.59 12.25 22.32 Y₂O₃ 2.33 5.62 2.14 7.32 0.00 Yb₂O₃ 0.00 0.00 0.00 0.00 1.24 WO₃ 0.00 0.00 0.00 0.00 0.00 Ta₂O₅ 0.00 1.24 0.00 0.00 0.00 Nb₂O₅ 3.65 2.58 3.25 0.53 2.63 ZrO₂ 6.25 7.00 4.50 2.51 4.37 TiO₂ 1.42 0.24 1.04 0.65 0.54 ZnO 18.82 18.48 20.05 25.53 14.53 Li₂O 0.36 0.25 0.30 0.22 0.18 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0.481 0 0 0 K2 0.255 0.256 0.330 0.334 0.497 K3 0.201 0.168 0.185 0.043 0.118 K4 0.372 0.289 0.366 0.307 0.468 K5 0.476 0.528 0.587 0.168 0.536 K6 0.915 1.089 0.880 0.833 0.504 K7 0.194 0.140 0.162 0.021 0.181 K8 0.280 0.085 0.242 0.551 0.170 K9 3.712 4.552 4.674 21.636 4.584 nd 1.79652 1.83658 1.81887 1.82562 1.78455 νd 45.36 42.33 42.58 41.28 46.30 Tg (° C.) 612.0 613.2 604.0 603.3 614.2 ρ(g/cm³) 4.72 4.80 4.83 4.79 4.85 λ₈₀/λ₅ 384/325 382/322 390/330 385/324 386/325 Upper limit of 1137 1135 1140 1130 1131 devitrification temperature (° C.) Devitrification A A A A A status Composition 6 7 8 9 10 SiO₂ 8.23 13.25 6.27 9.36 6.50 B₂O₃ 13.25 11.33 15.32 16.58 16.34 La₂O₃ 34.15 31.57 25.41 22.35 30.59 Gd₂O₃ 25.33 23.15 16.35 13.26 14.85 Y₂O₃ 1.25 3.15 0.25 7.26 4.15 Yb₂O₃ 0.00 0.00 0.41 0.00 0.00 WO₃ 0.00 0.00 2.64 0.00 6.60 Ta₂O₅ 0.00 0.00 0.00 0.47 0.00 Nb₂O₅ 1.58 1.24 5.81 4.15 0.70 ZrO₂ 1.34 1.00 3.35 5.32 4.85 TiO₂ 1.25 0.11 1.20 1.35 0.50 ZnO 13.24 14.58 21.35 16.28 14.28 Li₂O 0.38 0.62 0.28 0.16 0.60 Na₂O 0.00 0.00 0.00 1.25 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 2.21 0.00 RO 0.00 0.00 1.36 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.04 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0 0.113 0 K2 0.383 0.539 0.290 0.361 0.285 K3 0.062 0.054 0.3553 0.313 0.047 K4 0.417 0.400 0.389 0.309 0.230 K5 0.610 1.117 1.857 0.693 1.365 K6 0.616 0.593 0.989 0.628 0.625 K7 0.119 0.085 0.272 0.255 0.049 K8 0.442 0.081 0.171 0.246 0.417 K9 4.678 10.800 2.212 2.727 1.831 nd 1.84354 1.83124 1.78254 1.80053 1.81974 νd 42.52 42.40 45.25 46.26 42.83 Tg (° C.) 613.5 610.5 605.4 612.2 608.0 ρ(g/cm³) 4.88 4.79 4.78 4.75 4.79 λ₈₀/λ₅ 387/327 385/325 392/332 390/330 390/330 Upper limit of 1136 1128 1135 1136 1138 devitrification temperature (° C.) Devitrification A A A A A status

TABLE 2 Embodiment Composition 11 12 13 14 15 SiO₂ 16.23 9.24 7.26 6.35 7.50 B₂O₃ 20.17 15.30 21.52 17.60 15.30 La₂O₃ 21.35 36.24 25.17 23.50 29.50 Gd₂O₃ 12.30 18.24 14.22 13.25 18.13 Y₂O₃ 1.68 1.52 4.15 12.50 0.50 Yb₂O₃ 0.00 0.36 0.00 0.00 0.00 WO₃ 0.35 0.00 0.92 0.00 0.00 Ta₂O₅ 1.28 0.00 2.57 0.00 0.00 Nb₂O₅ 2.47 1.24 3.68 1.52 3.20 ZrO₂ 3.25 3.25 1.57 1.06 4.58 TiO₂ 0.57 1.45 0.36 0.60 1.64 ZnO 20.35 13.16 17.44 23.15 19.35 Li₂O 0.00 0.00 0.58 0.47 0.30 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.36 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.20 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0.518 0 0.698 0 0 K2 0.446 0.377 0.252 0.265 0.329 K3 0.201 0.068 0.259 0.1147 0.177 K4 0.348 0.326 0.327 0.2690 0.377 K5 1.073 0.264 3.715 0.9157 0.515 K6 0.559 0.536 0.606 0.9666 0.849 K7 0.121 0.094 0.211 0.0657 0.165 K8 0.188 0.539 0.089 0.283 0.339 K9 4.358 4.892 2.316 10.920 3.998 nd 1.78245 1.84742 1.80545 1.82542 1.82218 νd 44.25 41.66 45.20 42.36 42.69 Tg (° C.) 615.3 612.2 609.5 602.0 606.0 ρ(g/cm³) 4.80 4.75 4.85 4.78 4.86 λ₈₀/λ₅ 389/328 392/332 386/327 385/325 390/330 Upper limit of 1140 1137 1134 1140 1148 devitrification temperature (° C.) Devitrification A A A A A status Composition 16 17 18 19 20 SiO₂ 8.46 6.74 7.50 10.20 7.35 B₂O₃ 14.24 22.35 15.50 15.40 16.21 La₂O₃ 24.10 22.50 29.74 28.11 29.30 Gd₂O₃ 23.50 15.26 16.05 14.15 15.84 Y₂O₃ 6.24 5.14 2.14 9.45 2.05 Yb₂O₃ 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 0.00 0.00 1.00 Ta₂O₅ 0.00 0.00 1.00 0.00 0.00 Nb₂O₅ 4.15 2.52 2.50 4.15 2.50 ZrO₂ 1.50 3.47 4.50 2.23 4.35 TiO₂ 1.20 1.35 1.00 0.64 1.00 ZnO 16.33 20.32 19.77 15.4 20.10 Li₂O 0.28 0.35 0.30 0.27 0.30 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0.400 0 0 K2 0.373 0.232 0.326 0.398 0.312 K3 0.177 0.165 0.156 0.293 0.158 K4 0.437 0.356 0.335 0.274 0.336 K5 1.537 0.523 0.636 1.446 0.654 K6 0.719 0.699 0.860 0.602 0.853 K7 0.254 0.124 0.127 0.270 0.124 K8 0.224 0.349 0.286 0.134 0.286 K9 3.052 5.251 4.393 3.215 4.467 nd 1.79356 1.78658 1.79548 1.80124 1.81583 νd 45.30 45.28 45.36 45.50 42.94 Tg (° C.) 611.4 605.5 606.2 610.5 603.0 ρ(g/cm³) 4.88 4.75 4.85 4.82 4.83 λ₈₀/λ₅ 380/320 382/323 386/326 385/325 389/328 Upper limit of 1131 1134 1135 1130 1144 devitrification temperature (° C.) Devitrification A A A A A status

TABLE 3 Embodiment Composition 21 22 23 24 25 SiO₂ 6.50 7.35 5.82 8.16 7.36 B₂O₃ 15.64 18.21 22.47 17.24 20.14 La₂O₃ 30.52 24.18 26.73 23.54 27.32 Gd₂O₃ 18.34 15.33 16.33 17.15 13.25 Y₂O₃ 4.17 2.40 1.52 3.20 6.10 Yb₂O₃ 0.00 0.26 0.00 0.00 0.00 WO₃ 4.90 2.51 0.00 0.00 0.00 Ta₂O₅ 0.00 0.25 0.00 0.00 0.00 Nb₂O₅ 0.50 1.73 4.25 2.14 2.69 ZrO₂ 5.50 2.15 3.62 4.50 2.54 TiO₂ 1.00 0.78 1.52 1.43 1.33 ZnO 12.33 24.46 17.49 22.12 19.27 Li₂O 0.60 0.39 0.25 0.52 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0.145 0 0 0 K2 0.294 0.288 0.206 0.321 0.268 K3 0.027 0.113 0.260 0.125 0.203 K4 0.346 0.366 0.366 0.391 0.284 K5 0.831 1.532 0.827 0.361 0.695 K6 0.557 0.957 0.618 0.871 0.701 K7 0.041 0.071 0.243 0.097 0.140 K8 0.667 0.311 0.263 0.401 0.331 K9 1.927 4.641 3.031 6.196 4.794 nd 1.82174 1.82342 1.79152 1.79624 1.82357 νd 42.80 42.58 44.60 45.80 42.62 Tg (° C.) 613.0 603.5 606.6 602.0 608.4 ρ(g/cm³) 4.81 4.80 4.78 4.72 4.85 λ₈₀/λ₅ 390/330 388/328 389/330 383/323 388/328 Upper limit of 1146 1140 1142 1145 1128 devitrification temperature (° C.) Devitrification A A A A A status Composition 26 27 28 29 30 SiO₂ 11.20 5.15 9.23 6.35 10.24 B₂O₃ 11.54 18.20 13.25 19.33 14.23 La₂O₃ 33.26 28.41 25.16 26.54 25.36 Gd₂O₃ 14.40 16.30 15.25 15.26 26.12 Y₂O₃ 2.15 2.10 9.53 1.26 2.35 Yb₂O₃ 0.00 0.00 0.00 0.33 0.00 WO₃ 1.05 0.00 0.00 0.00 0.00 Ta₂O₅ 0.00 0.00 0.00 3.23 0.00 Nb₂O₅ 1.34 1.75 1.56 5.26 1.52 ZrO₂ 9.20 5.41 3.52 1.24 2.44 TiO₂ 0.58 2.88 3.34 0.81 1.50 ZnO 14.84 19.24 18.42 19.23 15.96 Li₂O 0.44 0.56 0.74 0.36 0.28 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.25 0.00 Al₂O₃ 0.00 0.00 0.00 0.55 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0 0.614 0 K2 0.493 0.221 0.411 0.247 0.418 K3 0.093 0.107 0.102 0.345 0.058 K4 0.289 0.348 0.305 0.354 0.485 K5 0.244 0.211 0.227 4.142 0.386 K6 0.653 0.824 0.819 0.749 0.652 K7 0.090 0.091 0.085 0.274 0.095 K8 0.302 0.622 0.682 0.133 0.497 K9 4.997 4.156 3.759 2.068 5.285 nd 1.81258 1.81891 1.78236 1.80245 1.83742 νd 41.26 42.87 46.50 43.40 41.25 Tg (° C.) 611.7 613 612.5 606.5 610.0 ρ(g/cm³) 4.86 4.79 4.83 4.75 4.83 λ₈₀/λ₅ 392/330 390/330 392/332 387/326 388/328 Upper limit of 1137 1135 1125 1138 1136 devitrification temperature (° C.) Devitrification A A A A A status

TABLE 4 Embodiment Composition 31 32 33 34 35 SiO₂ 7.50 6.47 8.24 6.33 7.34 B₂O₃ 17.90 17.26 15.30 18.25 16.62 La₂O₃ 24.10 27.35 29.23 28.40 26.48 Gd₂O₃ 20.24 17.52 15.50 18.20 16.35 Y₂O₃ 3.67 3.25 2.61 1.52 4.50 Yb₂O₃ 0.00 0.15 0.00 0.00 0.00 WO₃ 0.00 2.20 0.00 0.00 0.00 Ta₂O₅ 0.00 0.00 0.00 1.35 0.00 Nb₂O₅ 1.25 3.41 1.34 2.47 2.77 ZrO₂ 4.85 3.54 6.32 4.32 4.15 TiO₂ 0.71 0.80 0.48 0.56 0.37 ZnO 19.48 17.72 19.16 18.19 21.17 Li₂O 0.30 0.33 0.50 0.41 0.25 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 1.32 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00

TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0 0.547 0 K2 0.295 0.273 0.350 0.258 0.306 K3 0.062 0.195 0.087 0.136 0.169 K4 0.422 0.364 0.327 0.378 0.345 K5 0.225 1.293 0.197 0.783 0.613 K6 0.767 0.747 0.814 0.740 0.884 K7 0.064 0.192 0.070 0.136 0.131 K8 0.362 0.190 0.264 0.185 0.118 K9 9.939 2.764 10.527 4.153 6.742 nd 1.79341 1.80265 1.81427 1.79568 1.79645 νd 45.44 46.25 45.33 45.28 45.72 Tg (° C.) 604.0 606.0 605.4 603.2 602.1 ρ(g/cm³) 4.70 4.78 4.81 4.79 4.75 λ₈₀/λ₅ 380/320 386/326 380/320 382/322 381/320 Upper limit of 1140 1138 1132 1131 1125 devitrification temperature (° C.) Devitrification A A A A A status Composition 36 37 38 39 40 SiO₂ 7.50 9.14 7.69 5.15 12.20 B₂O₃ 17.90 13.25 15.25 20.32 14.30 La₂O₃ 28.10 25.26 30.20 29.80 27.34 Gd₂O₃ 20.00 16.40 18.15 16.20 14.50 Y₂O₃ 0.00 2.30 1.47 2.00 1.47 Yb₂O₃ 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 0.00 0.00 0.00 Ta₂O₅ 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 1.00 2.58 3.22 1.51 3.58 ZrO₂ 5.00 3.18 4.27 4.50 4.17 TiO₂ 0.70 0.68 0.49 1.00 0.59 ZnO 19.5 26.74 18.71 19.52 21.01 Li₂O 0.30 0.47 0.55 0.00 0.34 Na₂O 0.00 0.00 0.00 0.00 0.50 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0 0 0 K2 0.295 0.408 0.335 0.202 0.460 K3 0.050 0.157 0.177 0.093 0.247 K4 0.416 0.373 0.364 0.338 0.335 K5 0.175 0.668 0.677 0.275 0.752 K6 0.768 1.194 0.816 0.766 0.793 K7 0.051 0.097 0.172 0.077 0.170 K8 0.412 0.209 0.132 0.398 0.142 K9 11.471 8.202 5.043 7.777 5.038 nd 1.79375 1.80352 1.82305 1.79907 1.79584 νd 45.51 43.5 42.7 45.07 45.26 Tg (° C.) 599.0 600.0 603.5 615.0 608.5 ρ(g/cm³) 4.73 4.81 4.82 4.77 4.75 λ₈₀/λ₅ 380/320 383/323 388/328 384/317 385/325 Upper limit of 1130 1132 1135 1142 1140 devitrification temperature (° C.) Devitrification A A A A A status

TABLE 5 Embodiment Composition 41 42 43 44 45 SiO₂ 6.34 6.58 7.25 7.14 8.20 B₂O₃ 18.32 16.34 16.35 15.45 17.55 La₂O₃ 27.65 28.20 29.34 25.40 26.35 Gd₂O₃ 18.20 16.32 17.70 17.34 19.40 Y₂O₃ 2.95 2.47 2.34 3.60 1.24 Yb₂O₃ 0.20 0.00 0.00 0.00 0.00 WO₃ 0.00 2.36 0.00 0.00 0.00 Ta₂O₅ 0.00 0.45 0.00 0.00 0.00 Nb₂O₅ 3.54 3.15 2.24 1.58 2.46 ZrO₂ 3.85 5.74 4.16 4.18 2.25 TiO₂ 0.80 0.65 0.70 0.35 0.66 ZnO 17.75 17.36 19.37 24.49 21.37 Li₂O 0.40 0.38 0.55 0.47 0.52 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0.143 0 0 0 K2 0.257 0.287 0.307 0.316 0.318 K3 0.195 0.193 0.127 0.091 0.127 K4 0.373 0.347 0.358 0.374 0.413 K5 0.761 0.933 0.461 0.349 0.845 K6 0.720 0.757 0.821 1.084 0.830 K7 0.199 0.182 0.116 0.065 0.115 K8 0.184 0.171 0.238 0.181 0.212 K9 4.090 2.626 6.588 12.689 6.849 nd 1.79482 1.79556 1.82235 1.80822 1.82854 νd 45.66 45.37 42.77 44.52 43.16 Tg (° C.) 608.2 607.2 604.5 601.3 605.3 ρ(g/cm³) 4.81 4.80 4.79 4.81 4.85 λ₈₀/λ₅ 385/325 386/326 385/325 382/322 383/323 Upper limit of 1138 1135 1133 1136 1134 devitrification temperature (° C.) Devitrification A A A A A status Composition 46 47 48 49 50 SiO₂ 7.36 6.57 10.24 8.15 7.50 B₂O₃ 15.33 16.25 14.30 16.33 17.82 La₂O₃ 33.52 26.34 30.25 23.52 29.80 Gd₂O₃ 17.50 15.41 16.27 23.30 16.24 Y₂O₃ 2.56 3.75 4.55 2.35 2.50 Yb₂O₃ 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 3.40 0.00 0.00 0.00 Ta₂O₅ 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 1.24 2.17 1.52 3.25 1.10 ZrO₂ 4.15 3.50 3.65 5.30 4.25 TiO₂ 0.45 0.44 0.50 0.26 0.91 ZnO 17.61 20.32 18.22 17.24 19.28 Li₂O 0.28 0.39 0.50 0.30 0.60 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 1.20 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.26 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0 0 0 K2 0.324 0.288 0.417 0.333 0.296 K3 0.071 0.141 0.093 0.140 0.068 K4 0.327 0.339 0.319 0.474 0.335 K5 0.270 1.414 0.366 0.585 0.213 K6 0.776 0.890 0.743 0.704 0.762 K7 0.070 0.107 0.083 0.189 0.057 K8 0.266 0.169 0.248 0.074 0.453 K9 10.420 3.381 9.020 4.912 9.592 nd 1.83282 1.78968 1.82358 1.79622 1.79486 νd 42.58 45.25 42.85 45.57 47.60 Tg (° C.) 606.0 605.2 608.2 610.5 607.5 ρ(g/cm³) 4.82 4.75 4.78 4.78 4.82 λ₈₀/λ₅ 385/325 392/330 385/325 386/326 385//325 Upper limit of 1135 1140 1137 1137 1138 devitrification temperature (° C.) Devitrification A A A A A status

TABLE 6 Embodiment Composition 51 52 53 54 55 SiO₂ 7.56 6.48 6.70 7.25 8.24 B₂O₃ 16.35 15.27 15.34 17.10 16.26 La₂O₃ 28.50 29.34 28.50 27.50 30.30 Gd₂O₃ 15.34 16.42 16.55 20.20 17.45 Y₂O₃ 2.47 2.68 3.25 1.82 2.25 Yb₂O₃ 0.00 0.30 0.00 0.00 0.00 WO₃ 0.00 2.40 0.00 0.00 0.00 Ta₂O₅ 0.53 0.00 0.00 0.00 0.00 Nb₂O₅ 3.25 1.35 2.40 1.35 3.48 ZrO₂ 4.58 4.56 3.66 5.20 4.80 TiO₂ 1.25 0.68 1.24 0.74 0.36 ZnO 19.91 20.14 21.96 18.34 16.86 Li₂O 0.26 0.38 0.40 0.50 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0.163 0 0 0 0 K2 0.316 0.298 0.304 0.298 0.336 K3 0.212 0.082 0.145 0.067 0.199 K4 0.331 0.339 0.343 0.408 0.349 K5 0.648 0.716 0.490 0.227 0.674 K6 0.833 0.926 0.996 0.753 0.688 K7 0.163 0.067 0.109 0.074 0.206 K8 0.278 0.335 0.341 0.354 0.094 K9 3.958 4.546 6.033 8.775 4.391 nd 1.79568 1.82452 1.81265 1.82722 1.79628 νd 45.62 42.65 43.25 42.47 45.71 Tg (° C.) 605.4 604.5 603.2 607.5 612.5 ρ(g/cm³) 4.78 4.80 4.82 4.81 4.77 λ₈₀/λ₅ 383/323 388/325 385/325 382/320 386/325 Upper limit of 1130 1136 1138 1137 1142 devitrification temperature (° C.) Devitrification A A A A A status Composition 56 57 58 59 60 SiO₂ 5.24 7.58 7.34 6.49 9.15 B₂O₃ 15.28 18.36 16.30 18.22 17.20 La₂O₃ 33.25 26.44 27.59 27.45 26.50 Gd₂O₃ 16.25 16.50 18.20 19.20 16.33 Y₂O₃ 1.44 3.51 2.85 3.14 2.47 Yb₂O₃ 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 0.00 0.00 0.00 Ta₂O₅ 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 3.25 1.47 3.24 1.72 1.50 ZrO₂ 3.85 5.29 3.56 4.10 5.60 TiO₂ 0.74 1.40 1.05 0.84 1.24 ZnO 20.40 19.20 19.50 18.44 19.50 Li₂O 0.30 0.25 0.37 0.40 0.51 Na₂O 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 Al₂O₃ 0.00 0.00 0.00 0.00 0.00 RO 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 0.00 0.00 Bi₂O₃ 0.00 0.00 0.00 0.00 0.00 TeO₂ 0.00 0.00 0.00 0.00 0.00 Ga₂O₃ 0.00 0.00 0.00 0.00 0.00 Lu₂O₃ 0.00 0.00 0.00 0.00 0.00 GeO₂ 0.00 0.00 0.00 0.00 0.00 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 CeO₂ 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.00 0.00 0.00 0.00 0.00 F 0.00 0.00 0.00 0.00 0.00 Total 100.00 100.00 100.00 100.00 100.00 K1 0 0 0 0 0 K2 0.255 0.292 0.310 0.263 0.347 K3 0.200 0.089 0.178 0.090 0.092 K4 0.319 0.355 0.374 0.386 0.361 K5 0.708 0.220 0.703 6.348 0.219 K6 0.994 0.740 0.825 0.746 0.740 K7 0.159 0.077 0.166 0.093 0.077 K8 0.186 0.488 0.245 0.328 0.453 K9 5.113 6.690 4.545 7.203 7.117 nd 1.83052 1.82157 1.79518 1.82342 1.81859 νd 44.70 42.85 45.52 42.66 44.25 Tg (° C.) 605.2 604.5 605.2 604.3 602.5 ρ(g/cm³) 4.80 4.75 4.73 4.80 4.79 λ₈₀/λ₅ 385/325 386/335 380/320 385/325 384/320 Upper limit of 1136 1135 1130 1134 1135 devitrification temperature (° C.) Devitrification A A A A A status

[Glass Preform Embodiment]

The optical glass obtained in Embodiments 1-10 in Table 1 is cut into a predetermined size, and the release agent is uniformly coated on the surface. Then, the mold is heated and softened to be press-molded to produce a concave meniscus lens, a convex meniscus lens, a biconvex lens, a biconcave lens, a planoconvex lens, a planoconcave lens, and other various lens and prism preforms.

[Optical Element Embodiment]

The preforms obtained in the above-mentioned glass preform embodiment are annealed for fine-tuning while reducing the deformation inside the glass, so that the optical characteristics such as the refractive index are brought to the desired values.

Then, each of the preforms is ground and polished, and a variety of lenses and prisms such as concave meniscus lens, convex meniscus lens, biconvex lens, biconcave lens, planoconvex lens, and planoconcave lens are prepared. The anti-reflection film may be coated on the surface of the obtained optical element.

The present invention provides a high-refraction low-dispersion optical glass having a low cost and excellent chemical stability, with refractive index of 1.77-1.85 and Abbe number of 40-48, and an optical element made of the glass, capable of satisfying the needs of modern novel photoelectric products. 

1. An optical glass, comprising the following components by weight percentage: 4-20% of SiO₂; 8-24% of B₂O₃; 20-40% of La₂O₃; 11-30% of Gd₂O₃; 0-15% of Y₂O₃; 0-8% of TiO₂; 0-8% of Ta₂O₅; more than 0 but less than or equal to 8% of Nb₂O₅; less than 1 of Ta₂O₅/Nb₂O₅; more than 0 but less than or equal to 15% of ZrO₂; 11-30% of ZnO.
 2. The optical glass according to claim 1, further comprising the following components by weight percentage: 0-15% of WO₃; 0-10% of Al₂O₃; 0-10% of Yb₂O₃; 0-2% of Li₂O; 0-10% of Na₂O; 0-10% of K₂O; 0-1% of Sb₂O₃; 0-10% of RO, in which RO is one or more of MgO, CaO, SrO or BaO.
 3. An optical glass, comprising the following components by weight percentage: 4-20% of SiO₂; 8-24% of B₂O₃; 20-40% of La₂O₃; 11-30% of Gd₂O₃; 0-15% of Y₂O₃; 0-15% of WO₃; 0-8% of Ta₂O₅; more than 0 but less than or equal to 8% of Nb₂O₅; less than 1 of Ta₂O₅/Nb₂O₅; more than 0 but less than or equal to 15% of ZrO₂; 11-30% of ZnO; 0-8% of TiO₂; 0-10% of Al₂O₃; 0-10% of Yb₂O₃; 0-2% of Li₂O; 0-10% of Na₂O; 0-10% of K₂O; 0-1% of Sb₂O₃; 0-10% of RO, in which RO is one or more of MgO, CaO, SrO or BaO.
 4. The optical glass according to claim 1, wherein the content of each component satisfies one or more of the following 9 conditions: 1) Ta₂O₅/Nb₂O₅ is less than 0.8; 2) ZnO/(SiO₂+B₂O₃) is 0.3-2; 3) Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.2-0.55; 4) SiO₂/(SiO₂+B₂O₃) is 0.2-0.6; 5) Nb₂O₅/Gd₂O₃ is 0.01-0.45; 6) (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂) is 0.1-5; 7) Nb₂O₅/ZnO is 0.01-0.5; 8) TiO₂/(TiO₂+Nb₂O₅) is 0.01-0.8; 9) ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂) is above 1.8.
 5. The optical glass according to claim 1, comprising: 5-18% of SiO₂, and/or 10-23% of B₂O₃, and/or 20-35% of La₂O₃, and/or 11-25% of Gd₂O₃, and/or 0-10% of Y₂O₃, and/or 0-10% of WO₃, and/or 0-5% of Ta₂O₅, and/or 0.1-6% of Nb₂O₅, and/or 1-10% of ZrO₂, and/or 15-30% of ZnO; and/or 0-5% of TiO₂; and/or 0-5% of Al₂O₃; and/or 0-5% of Yb₂O₃; and/or 0-1% of Li₂O, and/or 0-5% of Na₂O; and/or 0-5% of K₂O; and/or 0-0.5% of Sb₂O₃, and/or 0-5% of RO.
 6. The optical glass according to claim 1, comprising: 6-15% of SiO₂, and/or 12-20% of B₂O₃, and/or 22-32% of La₂O₃, and/or 12-22% of Gd₂O₃, and/or 0-8% of Y₂O₃, and/or 0-7% of WO₃, and/or 2-8% of ZrO₂, and/or 15-25% of ZnO, and/or 0-2% of TiO₂.
 7. The optical glass according to claim 1, comprising: less than 0.5 of Ta₂O₅/Nb₂O₅, and/or 0.5-1.8 of ZnO/(SiO₂+B₂O₃), and/or 0.25-0.5 of Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃), and/or 0.23-0.5 of SiO₂/(SiO₂+B₂O₃), and/or 0.02-0.35 of Nb₂O₅/Gd₂O₃, and/or 0.1-3 of (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂), and/or 0.02-0.35 of Nb₂O₅/ZnO, and/or 0.05-0.7 of TiO₂/(TiO₂+Nb₂O₅), and/or 3-15 of ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂).
 8. The optical glass according to claim 1, comprising: 0.5-1.45 of ZnO/(SiO₂+B₂O₃); and/or 0.25-0.45 of Gd₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃), and/or 0.25-0.45 of SiO₂/(SiO₂+B₂O₃), and/or 0.05-0.25 of Nb₂O₅/Gd₂O₃, and/or 0.1-1 of (WO₃+Ta₂O₅+Nb₂O₅)/(ZrO₂+TiO₂), and/or 0.03-0.25 of Nb₂O₅/ZnO, and/or 0.1-0.6 of TiO₂/(TiO₂+Nb₂O₅), and/or 4-12 of ZnO/(WO₃+Ta₂O₅+Nb₂O₅+TiO₂).
 9. The optical glass according to claim 1, wherein: the total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O₅, WO₃, ZrO₂ and ZnO is above 95%, excluding Ta₂O₅.
 10. The optical glass according to claim 1, wherein: the total content of SiO₂, B₂O₃, La₂O₃, Gd₂O₃, Y₂O₃, TiO₂, Nb₂O₅, ZrO₂ and ZnO is above 99%.
 11. The optical glass according to claim 1, further comprising the following components by weight percentage: 0-10% of P₂O₅; 0-10% of Bi₂O₃; 0-10% of TeO₂; 0-10% of Ga₂O₃; 0-10% of Lu₂O₃; 0-8% of GeO₂; 0-1% of CeO₂; 0-1% of SnO₂; 0-10% of F.
 12. The optical glass according to claim 1, further comprising the following components by weight percentage: 0-5% of P₂O₅; 0-5% of Bi₂O₃; 0-5% of TeO₂; 0-5% of Ga₂O₃; 0-5% of Lu₂O₃; 0-5% of GeO₂; 0-0.5% of CeO₂; 0-0.5% of SnO₂; 0-5% of F.
 13. The optical glass according to claim 1, wherein the refractive index (nd) of the glass is 1.77-1.85, the Abbe number (vd) is 40-48, and the density (ρ) of the glass is below 5.00 g/cm³.
 14. The optical glass according to claim 1, wherein the corresponding wave length λ₈₀ is below 410 nm when the transmittance of the glass reaches 80%, the corresponding wave length λ₅ is below 350 nm when the transmittance reaches 5%, the upper limit of devitrification temperature is below 1160° C., and the glass transition temperature (Tg) is below 630° C.
 15. The optical glass according to claim 1, wherein the corresponding wave length λ₈₀ is below 400 nm when the transmittance of the glass reaches 80%, the corresponding wave length λ₅ is below 340 nm when the transmittance reaches 5%, the upper limit of devitrification temperature is below 1150° C., the glass transition temperature (Tg) is below 620° C., and the density (ρ) of the glass is below 4.90 g/cm³.
 16. A glass preform, made of the optical glass according to claim
 1. 17. An optical element, made of the optical glass according to claim
 1. 